Tuning Structure and Properties of a Ferromagnetic Organic Semiconductor via a Magnetic Field-Modified Reduction Process

Abstract

The development of novel synthesis and assembly strategies is critical to achieving a ferromagnetic organic semiconductor with high Curie temperature. In this study, we report a high magnetic field (HMF)-modified solvothermal approach for the reduction in neutral perylene diimide (PDI) into the dianion species to prepare the PDI magnets comprising radical anions after subsequent oxidation processes. The PDI materials, assembled from the dianion solution by an HMF-modified reduction, exhibit a smaller crystallite size and an enlarged distance of the π-π stacking in the PDI aggregates. Furthermore, the PDI magnets obtained from the process under a 9T field reveal weakened ferromagnetism and the rapid degradation of electrical conductivity compared to those prepared without a magnetic field. Based on spectral and structural characterizations, such performance deterioration originates from the enhanced instability of the radical anions exposed to air, as well as the decreased crystallinity for the radical PDIs synthesized from the HMF-modified reduction process. This work demonstrates that magnetic fields offer an effective way in the material synthesis process to manipulate the structure and magnetic properties of the radical-based organic magnets.

Keywords

• organic ferromagnetism
• high magnetic field
• organic semiconductors
• solvothermal approach
• radical anions