Statistical analysis of CO2/N2 gas separation permeance and selectivity using taguchi method

Abstract

The separation of CO2 from flue gases presents a crucial challenge that needs to be addressed. However, membrane processes offer a promising alternative solution. Polysulfone (PSF)membranes were prepared using N-methyl-2-pyrrolidone (NMP) and tetrahydrofuran (THF) using a dry–wet phase inversion technique. The membranes were fabricated with the selection of casting parameters, PSF concentration (20–30 wt%), solvent ratio of THF/NMP (0/100–35/65), and evaporation time (0–4 min). In this work, the interaction between these influencing factors during preparation and membrane performance was studied. Scanning electron microscopy (SEM) was used to characterize the membranes for morphological investigation. Taguchi statistical analysis was employed in the Minitab-19 software used for the design of the experiments in this study, and the responses of the CO2 permeance and CO2/N2 separation factor were analyzed and optimized based on the casting parameters. The results showed the CO2 permeance of the membranes was determined between 1.25 ± 0.04 and 8.47 ± 0.51GPU and selectivity was between 2.95 and 8.92.The statistical analysis indicated that casting conditions affect membrane performance in the following order: PSF concentration > solvent ratio > evaporation time. The optimum parameters for casting solution were the PSF concentration of 20 wt%, THF/NMP ratio of 17.5/82.5, and evaporation time of 4 min. The selected method also reinforces the connection between membrane casting parameters and the observed outcomes in terms of permeation and morphology.

Keywords

• Flue gases
• Polysulfone (PSF)
• Optemaztion parameters
• Taguchi
• Solvent ratio