Structural, Mechanical and Flammability Characterization of Crosslinked Talc Composites with Different Particle Sizes

Abstract

The influence of filler particle size on selected physicochemical and functional properties of polymer composites was analyzed. The following test was carried out for the system: the bisphenol A glycerolate (1 glycerol/phenol) di-methacrylate (BPA.DM) was subjected to UV-polymerization in bulk with N-vinyl-2-pyrrolidone (NVP) as a polymer matrix and talc with particle sizes ranging from ≤8 to 710 µm as a non-toxic and cheap mineral filler. An effective method of preparing cross-linked polymeric composites with talc was developed. The obtained samples were subjected to structural analysis and the thermal, mechanical and flammability properties were assessed. It has been empirically confirmed that the talc particles are incorporated into the composite structure. However, with increasing particle size, the composite heterogeneity increases. In the case of the developed method of sample production, homogeneous systems were obtained for particles in the ≤8–250 µm range. The surface roughness of the samples correlates directly with the size of talc particles. The value of Young’s modulus during the axial stretching of samples decreases with the increasing size of talc particles. For the composites containing ≤15 and ≤35 µm talc particles, the highest values were obtained under bending conditions. There was no equivocal effect of particle size on the composites’ swelling in water. The addition of talc reduces the flame height and intensity slightly. The biggest difference was obtained for the composites containing relatively large talc particles. It was proved that the selected properties of polymer composites can be controlled depending on the size of the talc particles.

Keywords

• talc
• methacrylate
• N-vinyl-2-pyrrolidone
• crosslinked composites
• thermal and mechanical properties
• flammability tests