Boletín de la Sociedad Española de Cerámica y Vidrio (Apr 2004)
Nuevos avances en la formación de fases interestratificadas durante el proceso de deshidratación-rehidratación de vermiculitas-Mg: Influencia de la presión de vacío, temperatura y composición
Abstract
New results obtained from X-ray diffraction about structural transformations induced by vacuum between the different hydration states of three vermiculites (powdered and flake samples) with different composition and origin, are presented. The dehydration process of the vermiculites under vacuum has been proved to be the same as that of temperature but with a different evolution through the different hydration states, although the zero-water layer hydration state has been not observed. The sample from Sta. Olalla, with the major content of Mg in the interlayer, exhibits the most complex behaviour.<br><br>Se presentan nuevos resultados obtenidos mediante difracción de rayos X sobre las transformaciones estructurales que se producen en vermiculitas (en polvo y en lámina de exfoliación) con distinta composición y procedencia, cuando se las somete a condiciones diferentes de presión y temperatura. El proceso de deshidratación de las vermiculitas que se produce bajo vacío es similar al que tiene lugar con aumento de la temperatura, es decir, se lleva a cabo mediante la formación de fases interestratificadas, aunque su evolución es diferente ya que nunca se alcanza el estado de hidratación de cero capas de agua en el espacio interlaminar. La muestra de Sta. Olalla (Huelva), con el mayor contenido de magnesio en dicho espacio, muestra el comportamiento más complejo.