Evaluation of the impact energy of the samples produced by the additive manufacturing technology

Abstract

The article covered the evaluation of the impact energy, notch toughness and morphology of the fracture surfaces of the specimens manufactured by the Direct Metal Laser Sintering Technology. Specimens without heat treatment with no notch were not broken through in course of testing, therefore there was no fracture surface present. The heat treatment resulted in the increase in hardness values. The values of impact energy after the heat treatment was approximately 60 % lower. Ductile intergranular fracture with more or less segmented dimple morphology appeared in every specimen. At places where the internal plastic bond was resisting the test, cracks remaining after particles broke away from the surface can be seen as craters.

Keywords

• metal powder
• mechanical properties
• impact energy
• fracture
• surface