Inhibition of Carbide Growth by Sr in High-Alloyed White Cast Iron

Abstract

Chromium cast irons have gained a well-settled position among wear-resistant materials where a low manufacturing cost is one of the key factors. The wear properties of these alloys are commonly improved by the addition of carbide-forming inoculating elements such as Ti, V, B, etc., allowing the formation of underlays for the precipitation of both M7C3 carbides and austenite. On the other hand, Sr may work as a surface-active element that adsorbs on the surface of the growing crystal, inhibiting its growth. This mechanism may support the M7C3 nucleation process. The experiment was conducted on near-eutectic chromium cast irons with 20% of Cr and 2.5–3% of C. Different amounts of strontium were used as the microstructure modifier. The improvement of carbides’ stereological parameters and collocation resulted in the improvement in functional properties—wear resistance and impact strength without a significant increase in hardness as well as a decrease in carbide phase. Two types of wear studies with a modified pin-on-disc method and tests in reciprocating motion of samples in the metal-mineral system were performed. The results showed that addition modification with Sr can increase the impact strength of the alloy. EDS analysis of the samples provided results similar to hypoeutectic Al-Si alloys modified with strontium.

Keywords

• white cast iron
• crystallization
• modification
• wear resistance