Impact of Zirconium on the Structural and Mechanical Properties of Commercial AlSi10MgCu Alloys

Abstract

The impact of small addition of zirconium in hypoeutectic commercial AlSi10MgCu alloys on their mechanical properties (hardness) in as cast and thermally treated conditions was investigated. Small addition of zirconium does not change significantly the as cast and heat-treated microstructure of investigated alloys except to reduce the SDAS and grain size of primary α-aluminium phases. Addition of zirconium up to 0.14 wt. percentage increases the hardness of investigated alloys in as cast conditions. The increase in the hardness of samples after various solid solution times can correlate very well with the formation of small needle like coherent Al3Zr particles.

Keywords

• zirconium
• alsi10mgcu alloy
• hardness
• solid solution treatment