The Effect of Thickness on the Sealing Ability of CEM Cement as a Root-end Filling Material

Abstract

Background and aims. Different materials have been used for root-end filling during surgical endodontic treatment. The aim of this in vitro study was to evaluate the dye penetration in different thicknesses of calcium enriched mixture (CEM) cement as root-end filling material. Materials and methods. Following root canal filling in 70 extracted human single-rooted premolar teeth, the apical 3 mm of their root-ends was resected; the root-end cavities with depths of 1, 2 and 3 mm were prepared by ultrasonic retrotips and filled with CEM cement. After setting of cement, the roots were immersed in 2% Rhodamine B and the dye leakage was measured under stereomicroscope (×16) using Image J software. The data were analyzed by one-way ANOVA and Bon-ferroni post hoc tests at 5% significance level. Results. The means and standard deviations of dye penetration in the 1, 2, and 3 mm groups were 3395.5 ± 1893.4, 3410.4 ± 1440.5, and 2581.6 ± 1852.9 μm, respectively. The one-way ANOVA analysis indicated significant differences (P < 0.001); however, the Bonferroni post hoc test revealed that only the positive control group differed significantly from the experimental groups (P < 0.001). Conclusion. The findings demonstrated CEM cement to have an adequate root-end sealing ability in 3-mm thickness.

Keywords

• Calcium enriched mixture
• CEM cement
• Leakage
• root-end filling materials
• sealing efficacy