Fabrication of Porous Recycled HDPE Biocomposites Foam: Effect of Rice Husk Filler Contents and Surface Treatments on the Mechanical Properties

Abstract

In this study, a biodegradable, cheap and durable recycled high-density polyethylene (rHDPE) polymer reinforced with rice husk (RH) fibre was fabricated into a foam structure through several processes, including extrusion, internal mixing and hot pressing. The effect of filler loading on the properties of the foam and the influence of RH surface treatments on the filler−matrix adhesion and mechanical properties of the composite foam were investigated. The morphological examination shows that 50 wt.% filler content resulted in an effective dispersion of cells with the smallest cell size (58.3 µm) and the highest density (7.62 × 1011 sel/cm3). This small cell size benefits the mechanical properties. Results indicate that the tensile strength and the Young’s modulus of the alkali-treated RH/rHDPE composite foam are the highest amongst the treatments (10.83 MPa and 858 MPa, respectively), followed by UV/O3, which has shown considerable increments compared with the untreated composite. The flexural and impact tests also show the increment in strength for the composite foam after chemical treatment. Although the UV/O3 surface treatment has minor influence on the mechanical enhancement of the composite foam, this method may be a reliable surface treatment of the fibre-reinforced composite.

Keywords

• rice husk
• recycled hdpe polymer
• biocomposite foam
• surface treatment
• mechanical properties
• filler–matrix adhesion