The Oxide Scales Formed on Different Co-Ni Based Superalloys During Isothermal Oxidation at 800 and 900°C

Abstract

In this investigation, the formation of oxide scales on different Co-Ni based superalloys of γ–γ′ type was analyzed. Co-20Ni-7Al-7W (at. %) alloy as well as its W-free modifications based on Co-Ni-Al-Mo-Nb and Co-Ni-Al-Ta systems was analyzed under conditions of high temperature oxidation at 800 and 900°C. Therefore, the alloys were isothermally oxidized at selected temperatures for 100 h in laboratory furnace. Afterwards, the oxidation products were evaluated by means of X-ray diffraction (XRD), optical microscopy (OM) and scanning electron microscopy (SEM). The performed tests showed that W-free alloys exhibit worse oxidation resistance compared to those of Co-Ni-Al-W alloys. After oxidation at 900°C, all alloys were prone of oxide spallation. The scales characterized by oxide peeling were mostly composed of complex Co-based oxides, including CoWO4, CoTa2O6, Co2Mo3O8, CoNb2O6.

Keywords

• γ–γ′ cobalt-based superalloys
• high temperature oxidation
• co-ni superalloy
• w-free cobalt superalloys