The Impact of Citric Acid Solution on Hydraulic Calcium Silicate-Based Sealers and Root Dentin: A Preliminary Assessment
Abstract
Hydraulic calcium silicate-based (HCS) sealers have recently gained tremendous popularity due to their unique properties. However, their removal during endodontic retreatment is challenging. The solvent, which could chemically deteriorate the material, would be highly desirable for endodontic retreatment procedures. This preliminary study assessed the interplay and dissolving capability of 10% and 20% citric acid, compared to 17% EDTA, on commonly used HCS sealers (AH Plus Bioceramic Sealer, Bio-C Sealer, BioRoot RCS, TotalFill BC Sealer), and evaluated the potential impact of these solutions on root dentin structure. The interaction between tested sealers and irrigating solutions was photographed, and solubility-related mass changes were determined. The surface morphology of treated filling materials and dentin was evaluated using a scanning electron microscope (SEM). One-way analysis of variance (ANOVA) along with Tukey’s test were used to detect the statistically significant differences among groups at the confidence level of 0.95. Intense gas release was observed during the interaction of HCS materials and citric acid, with no evidently visible “bubbling” after the immersion in EDTA. The mass loss of HCS sealers equally confirmed the significantly higher dissolving characteristics of 10% and 20% citric acid solutions compared to EDTA. The surface structural changes, associated with pore and crack formation, were mainly seen for HCS sealers exposed to citric acid. Meanwhile, no severe erosion was detected for dentin after root canal preparation with 10% and 20% citric acid solutions. These findings demonstrate that citric acid has the potential to dissolve HCS sealers with minimal or no negative impact on root dentin, suggesting citric acid as a solvent for HCS sealers in endodontic retreatment procedures.
Keywords