Transparent conductors (TC) have been widely applied in a wide range of optoelectronic devices. Nevertheless, different transparent spectral bands are always needed for particular applications. In this work, indium tin oxide (ITO)-free TCs with tunable transparent bands based on the film structure of TiO2/Ag/AZO (Al-doped ZnO) were designed by the transfer matrix method and deposited by magnetron sputtering. The transparent spectra and figure-of-merit (FOM) were effectively adjusted by precisely controlling the Ag layer’s thickness. The fabricated as-deposited samples exhibited an average optical transmittance larger than 88.3% (400–700 nm), a sheet resistance lower than 7.7 Ω.sq−1, a low surface roughness of about 1.4 nm, and mechanical stability upon 1000 bending cycles. Moreover, the samples were able to hold optical and electrical properties after annealing at 300 °C for 60 min, but failed at 400 °C even for 30 min.