Degradation Mechanisms of Transparent Polyurethane Interlayer under UV Irradiation

Abstract

According to the ageing problem of laminated transparency, the trasparent polyurethane film used as interlayer had been irradiated by fluorescent ultraviolet lamp for 0 h, 200 h, 300 h, and 500 h respectively. With the aid of ultraviolet/visible spectrophotometer, FTIR and SEM etc., the color, structure and morphology of the materials were studied. SEM shows that when the irradiation time is increased to 500 h, the film surface cracks. The UV degradation mechanisms are that -CH2- of the position connecting the O and N from hard segment and the soft segment are easy to oxidize and produce hydrogen peroxide under UV and oxygen, which is furtherly oxidized to CO, and some part of the C-O and C-N bonds is cracked through β scission, and then the materials are fractured.

Keywords

• transparent polyurethane interlayer
• UV irradiation
• FTIR
• degradation mechanisms