Inhibited Surface Diffusion in Nanoporous Multi-Principal Element Alloy Thin Films Prepared by Vacuum Thermal Dealloying

Abstract

Nanoporous structures with 3D interconnected networks are traditionally made by dealloying a binary precursor. Certain approaches for fabricating these materials have been applied to refractory multi-principal element alloys (RMPEAs), which can be suitable candidates for high-temperature applications. In this study, nanoporous refractory multi-principal element alloys (np-RMPEAs) were fabricated from magnesium-based thin films (VMoNbTaMg) that had been prepared by magnetron sputtering. Vacuum thermal dealloying (VTD), which involves sublimation of a higher vapor pressure element, is a novel technique for synthesizing nanoporous refractory elements that are prone to oxidation. When VMoNbTaMg was heated under vacuum, a nanoporous structure was created by the sublimation of the highest vapor pressure element (Mg). X-ray photoelectron spectroscopy depth profiling indicated significantly less ligament oxidation during VTD as compared to traditional dealloying methods. Furthermore, np-RMPEAs exhibited outstanding stability against coarsening, retaining smaller ligaments (~25 nm) at elevated temperature (700 °C) for a prolonged period (48 h).

Keywords

• vacuum thermal dealloying
• multi-principal element alloy
• nanoporous
• surface diffusion