The Sticking Out Mechanism and Growth of TiB Whiskers from TiBw/Ti-6Al-4V Composites during Sintering

Abstract

The process of TiB whiskers (TiBw) squeezed out and the growth of sticking out TiBw were investigated in TiBw/Ti-6Al-4V composites via adding 5 vol% TiB2 powders. TiB2 distributed along the surface of Ti-6Al-4V powders by low energy milling, resulted in the enrichment region of B and Ti elements. During sintering, TiBw nucleated and grew along the [010] direction with the diffusion of B and Ti atoms in the enrichment region. Due to larger thermal expansion ratio of TiBw, the TiBw were squeezed out from the Ti matrix, and the sticking out TiBw grew gradually with the diffusion of B and Ti atoms from the enrichment region. Because of the high interfacial strength between TiBw and Ti matrix, the matrix adhered to TiBw, and hindered the squeezing out of TiBw. Eventually, the cone TiBw stuck out the Ti matrix, and the other end of TiBw pinned in Ti matrix. Moreover, the diameter of TiBw near surface between TiB2 and Ti matrix was larger than other areas, resulting from the high concentration of B and Ti atoms. The solubilized B atoms near TiBw were absorbed by TiBw, which was considered as the other B source of TiBw.

Keywords

• TiB whiskers
• squeezed out
• sticking out
• enrichment region
• thermal expansion ratio