Journal of Pharmacy and Bioallied Sciences (Jan 2017)

Effect of biomineralization ability on push-out strength of proroot mineral trioxide aggregate, mineral trioxide aggregate branco, and calcium phosphate cement on dentin: An In vitro evaluation

  • Vanita D Revankar,
  • M S Prathap,
  • K Harish Kumar Shetty,
  • Azmin Shahul,
  • K Sahana

DOI
https://doi.org/10.4103/jpbs.JPBS_120_17
Journal volume & issue
Vol. 9, no. 5
pp. 121 – 126

Abstract

Read online

Context: Biomineralization is a process which leads to the formation of an interfacial layer with tag-like structures at the cement-dentin interface. It is due to interaction of mineral trioxide aggregate (MTA) and Portland cement with dentin in phosphate-buffered solution (PBS). This study is aimed to evaluate the effect of influence of biomineralization process on push-out bond strength of ProRoot MTA (Dentsply Tulsa Dental, Tulsa, OK, USA), MTA Branco (Angelus Soluc¸o˜es Odontolo´gicas, Londrina, PR, Brazil) and calcium phosphate cement (BioGraft CPC). Aim: The aim of this study was to evaluate the effect of biomineralization process on the push-out strength of ProRoot MTA, MTA Branco, and CPC after mixing with 0.2% chlorhexidine gluconate solution (0.2% CHX) and 2% lidocaine solution (2% LA) on the bond strength of MTA-dentin. Materials and Methods: Dentin discs with uniform cavities were restored with ProRoot MTA, MTA Branco, and calcium phosphate cement after mixing with 0.2% CHX solution and 2% lidocaine solution. The samples were uniformly distributed into two groups. Experimental group being immersed in PBS solution and control group being immersed in saline for 2 months. Instron testing machine (Model 4444; Instron Corp., Canton, MA, USA) was used to determine the bond strength. Statistical Analysis Used: A two-way analysis of variance and post hoc analysis by Bonferroni test. Results: All samples immersed in experimental group displayed a significantly greater resistance to displacement than that observed for the samples in control group (P < 0.05). MTAs displayed a significantly greater resistance to displacement than calcium phosphate cements. Conclusion: The main conclusion of this study was that the push-out bond strength of the cements, mainly the MTA groups, was positively influenced by the biomineralization process.

Keywords