Focusing on the corrosion resistance enhancement of HRB400 rebar by Cr addition in the marine environment

Abstract

The corrosion resistance of Cr reinforced HRB400 rebar in the marine environment was investigated. The addition of Cr increases the amount of Cr(OH)3 and α-FeOOH in the passivate film, resulting in a denser passivate film structure. This enhanced passivation film inhibits localized corrosion. The pitting potential and critical chloride concentration (CTL) of the steel increased with the increase in chromium content, indicating improved corrosion resistance of the steel. On the other hand, an increase in the concentration of Cl- in solution leads to a decrease in the pitting potential and resistance of the steel, which reduces the corrosion resistance. At higher Cl- concentrations, the Cl- ions form an electrochemical interface with the steel surface, resulting in a sharp decrease in the Rf value. In addition, the gradual decrease in solution pH leads to a decrease in the pitting potential and CTL of HRB400 and 1.5Cr steel. The corrosion resistance was also found to be reduced, pH reduction accelerated the intrusion of chloride ions, which led to a severe breakdown of the passivation film.

Keywords

• Steel
• EIS
• Passive film
• Pitting corrosion