Eye-Visible Oxygen Sensing via In-Situ Synthesizing Blue-Emitting Cu(I) Cluster in Red-Emitting COF: Characterization and Performance

Abstract

Covalent organic frameworks (COFs) have shown virtues of well-defined and uniform pores with structural diversity, including the shape, size and even chemical nature of pores. These features are excellent for the application of O2 gas optical sensors. In this paper, two oxygen probes based on halogen-bridged Cu cluster were in-situ synthesized in the micropores of COFs, to allow a uniform distribution. The resulting composite samples were characterized in detail to confirm the successful probe loading. The doping level was determined as ~22%. The halogen-bridged Cu clusters showed blue emission peaking at ~440 nm, while COF host showed red emission peaking at 630 nm. These halogen-bridged Cu clusters had long emissive lifetime of ~6.7 μs and high emission quantum yield of 0.30 in pure N2 atmosphere. Given pure O2 atmosphere, lifetime and quantum yield were quenched to 2.5 μs and 0.11, showing oxygen-sensing possibility. A linear oxygen-sensing calibration curve was observed, with sensitivity of 12.25, response time of 13 s and recovery time of 38 s. Sample emission color was changed from blue to red when testing atmosphere was changed from pure N2 to pure O2, which was detectable by eyes.

Keywords

• COF
• micropores
• oxygen-sensing
• in-situ synthesis
• halogen-bridged cluster