Effect of Oxygen and Moisture on the Friction and Wear of Carbon Fiber-Reinforced Polymers

Abstract

Carbon fiber-reinforced polytetrafluoroethylene (CF/PTFE) composites are frequently used in tribological dry gas applications, such as in dynamic seals in reciprocating hydrogen gas compressors and Stirling engines, due to their superior friction and wear. Due to the increasing concerns regarding fluoropolymers as possible pollutants of harmful per- and poly-fluoroalkyl substances (PFAS) emissions, replacements for PTFE should be investigated. The literature indicates that CF-reinforced polyetheretherketone (CF/PEEK) may have similar favorable tribological properties to CF/PTFE. However, the tribological behavior of CF/PEEK in dry gas is poorly understood, and no direct comparison has been made between the two materials. The aim of this study was to compare the effect of oxygen and moisture on the friction and wear of CF/PTFE and CF/PEEK. Tribological tests were carried out with a tri-pin-on-disc tribometer in a nitrogen environment with individually controlled contents of oxygen and moisture. The results showed that the effect of oxygen and moisture are distinctly different for CF/PTFE and CF/PEEK. While CF/PTFE performs best in oxygen-deficient environments, CF/PEEK performs best in moisture-enriched environments. Complementary tests with a PTFE composite filled with both CF and PEEK suggested that the environmental sensitivity can be significantly reduced by combining the two polymers.

Keywords

• polymer composite
• dry gas
• environment
• ultralow wear