Magnetic properties and nanocrystallization behavior of Co-based amorphous alloy

Abstract

The magnetic properties of the amorphous Co57Fe5Ni10Si11B17 alloy have been studied by a vibrating sample magnetometer. The temperature dependence of saturation magnetization was measured and the Curie point and crystallization onset temperature were determined as 560 K and 760 K respectively. The coercive force was obtained as 200 A/m and saturation magnetization - 65 Am2 /kg. The alloy was produced in the form of a ribbon thickness of 30 µm using the melt spinning method, and its internal amorphous structure was examined by the X-ray diffraction method. The crystallization behavior of the alloy was studied using series of isothermal annealing of the samples of the alloy at temperatures in the range of 723-1023 K for different exposures (up to 240 minutes) and nanocrystalline phases were detected by the X-ray diffraction analysis.

Keywords

• co-based amorphous alloy
• dta
• thermo-magnetic curves
• hysteresis
• magnetic properties
• x-ray diffraction
• nanocrystallization