Thermal-Driven Formation of Silver Clusters Inside Na/Li FAUY Zeolites for Formaldehyde Detection

Abstract

In this research, the LiY zeolite was firstly synthesized by using NaY as the parent zeolite; thereafter, the LiYAg and NaYAg zeolites created for formaldehyde gas detection were prepared with further Ag+-Li+/Na+ exchange and a mild thermal treatment at 300 °C to promote the formation of luminescent Ag CLs. The spectra experimental results indicated that Ag CLs showed stronger and blue-shifted emissions in LiYAg compared with in NaYAg, and the emission intensity of Ag CLs in both zeolites monotonously decreased when exposed to increasing formaldehyde gas content. Moreover, the linear dependence of the Ag CLs’ emission intensity variation on formaldehyde content indicated a reliable method for fast and sensitive formaldehyde detection. According to the XPS, UV–vis absorption, and N2 adsorption–desorption isotherm studies, the formaldehyde-gas-induced luminescence quenching of Ag CLs is due to the formation of Ag2O and Ag NPs, in which the higher content of Ag+/Ag0 redox couples in LiYAg and larger surface area of NaYAg benefit the precise detection of formaldehyde gas in low- and high-content ranges, respectively. Furthermore, the blue-shifted peak position and widened FWHM of Ag CLs can also be used for the indication of formaldehyde gas and the detection limit of NaYAg and LiYAg, which both meet with the standards of the WHO and OSHA.

Keywords

• FAUY zeolite
• silver clusters
• luminescence property
• formaldehyde detection
• auger parameter