The Influence of the Hot-Rolling Temperature on the Microstructure and Mechanical Properties of Ti-Nb Microalloyed 21%Cr Ferritic Stainless Steel

Abstract

Microalloying and heat treatment are essential processing techniques for ferritic stainless steel (FSS). Three different compositions of 21%Cr FSS with 0.28Ti, 0.21Ti + 0.05Nb, and 1.05Ti + 0.17Nb were prepared. The interaction effects of the Nb and Ti contents and hot-rolling annealing on the microstructure, mechanical properties, and precipitate phases of FSS were studied. The microstructure, crystal structure, and precipitation phase of steel at 930, 980, and 1030 °C with Ti-Nb microalloying were investigated using an optical microscope (OM), X-ray diffractometer (XRD), and scanning electron microscope (SEM). The room-temperature tensile properties, surface roughness, and hardness were tested separately. This study found that the composite addition of Ti and Nb had a dual effect of fine-grain strengthening and precipitation strengthening. The 1.05Ti + 0.17Nb steel specimen had a moderate grain size and the best uniformity after hot rolling at 980 °C. The tensile strength and elongation were 454 MPa and 34.2%, which achieved an optimal balance between strength and plasticity.

Keywords

• FSS
• hot-rolling temperature
• Ti-Nb microalloying
• microstructure
• mechanical property