High-Performance Ni-SiC Coatings Fabricated by Flash Heating

Abstract

In this research, a novel flash heating coating application technique was utilized to create Ni-SiC coatings on carbon steel substrates with SiC contents much higher than is achievable using certain conventional coating techniques. Hardness profiles showed that the coatings improved the substrate by as much as 121%, without affecting the substrate. Tribotests showed that the wear performance was improved by as much as 4.7× in terms of the wear rate (mm3/N·m) for the same coating when using an Al2O3 counterpart. Pure SiC coatings as a reference were also fabricated. However, the SiC coatings experienced elemental diffusion of Fe from the carbon steel substrate into the coating during fabrication. This occurred due to the increased heat input required for pure SiC to fuse to the substrate compared to the Ni-SiC coatings and resulted in decreased tribological performance. Diffusion of Fe into the coating weakened the coating’s hardness and reduced the resistance to wear. It was concluded that ceramic–metallic composite coatings can successfully be fabricated utilizing this novel flash heating technique to improve the wear resistance of ceramic counterparts.

Keywords

• Ni-SiC coatings
• wear resistance
• tribology
• high hardness