Eco Valorization of <i>Eucalyptus globulus</i> Bark and Branches through Liquefaction

Abstract

Eucalyptus globulus forest residues, bark, and branches, were characterized by wet chemistry methods and involved in the liquefaction process using a glycerol-ethylene glycol reaction mixture (1:1, v/v) catalyzed by strong mineral acid (3% H2SO4) or strong mineral base (6% KOH). The effect of the reaction conditions (temperature and duration) and the particle size on the yield of liquefied products have been evaluated. Acid catalysis revealed remarkably higher yields (25–50%) than when using basic catalyst. It was considered that bark was more vulnerable to liquefaction with respect to particle size than branches. Too high temperatures (>180 °C) are not advantageous regarding the liquefaction yields and, therefore, temperatures around 160–180 °C would be preferable. The best yield for the bark sample (>80 mesh fraction) was obtained at 180 °C for 60 min (61.6%), while for the branches the best yield was obtained at 160 °C for 60 min (62.2%). Under compromised conditions (180 °C for 60 min), the fine fraction (>80 mesh) of bark and branches did not show significant differences between their liquefaction yields and can be processed together while adjusting the suitable processing time. The main advantage of the use of these residues instead of solid wood is that it would bring the Forest managing companies a much higher income for their wastes that are usually burned and the use of lignocellulosic materials in detriment of petroleum-based materials for the production of polymers would make industry less dependent on oil prices fluctuations.

Keywords

• bark
• branches
• <i>Eucalyptus globulus</i>
• low temperature liquefaction
• optimization
• wastes