This work presents the results of the partial substitution of Portland cement (PC) by natural fluorite (NF) and calcined fluorite (CF) in mortars, at 10%, 25% and 40%. To meet these objectives, a sample of fluorite was initially studied by XRD, SEM and Raman Spectroscopy (RS). A chemical quality analysis (CQA) and a chemical pozzolanicity test (CPT) at 8 and 15 days were carried out in a second stage to establish the pozzolanic properties of the investigated sample. Finally, a mechanical compressive strength test (MCST) at 7, 28 and 90 days was carried out on specimens made up with PC/NF and PC/CF mixes, at a ratio of 10%, 25% and 40%. XRD, SEM and RS results indicated fluorite as the major mineralogical phase. The CPT and CQA showed an increase in the pozzolanicity of the samples from 8 to 15 days. The MCST showed an increase in compressive strength from 7 to 90 days for both PC/NF and PC/CF specimens. The results obtained establish that fluorite produces positive effects in the mortar and contributes to the gain of mechanical strength over time, being a suitable material for the manufacture of cements with pozzolanic addition with a reduction of CO2 emissions, and by reducing the energy costs of production.