Enhanced Molten Salt Resistance by Sidewall Pores Repair during Fs Laser Drilling of a Thermal Barrier-Coated Superalloy

Abstract

In this study, a novel laser-modified drilling method was used to manufacture cooling holes through thermal barrier coatings (TBCs). Due to the “cooling processing” properties during low-frequency femtosecond (LF-fs) laser drilling, the exposure of the sidewall pores, and the interlayer clearance, the inherent characteristics of plasma-sprayed coatings induced sidewall defects in the drilled holes. After drilling, a high-frequency fs (HF-fs) laser was used to repair the sidewall pores and interlayer clearance of the drilled ceramic holes. Then, the pores and microcracks were healed by local melting using the laser. Moreover, instead of obtaining laser-induced periodic surface structures (LIPSSs), refined and homogeneous grains were produced by the HF-fs laser repair treatment at high transient pressure and temperature. The results from a high-temperature corrosion test showed that healing of the open pores and microstructural improvement in the ceramic hole walls prevented the out-diffusion of Y2O3 stabilizers and the penetration of molten salt, resulting in less corrosive products and producing corresponding phase-transformation stress. Thus, reducing the stabilizer consumption can moderate corrosion fatigue and prolong the lifetime of a cooling hole and TBCs under service.

Keywords

• laser processing
• TBCs
• pore repairing
• thermal effect
• corrosion