Boletín de la Sociedad Española de Cerámica y Vidrio (Aug 2012)
Sinterización reactiva de Hexaluminato de Calcio mediante “Spark Plasma Sintering”
Abstract
Calcium hexaluminate (CaAl<sub>12</sub>O<sub>19</sub>) is the most alumina-rich intermediate compound of the CaO-Al<sub>2</sub>O<sub>3</sub> system. The formation of this aluminate is produced by the reaction between calcium oxide and alumina with the consequent formation of intermediates compounds with lower alumina content with increasing temperature (CaAl<sub>2</sub>O<sub>4</sub>, CaAl<sub>4</sub>O<sub>7</sub>…). In this study we studied the variation of sintering parameters for obtaining dense and pure calcium hexaluminate by reaction sintering by Spark Plasma Sintering (SPS). A mixing of Al<sub>2</sub>O<sub>3</sub> and CaCO<sub>3</sub> were used as reactive. Final densities close to the theoretical and phase transformation over 93% were achieved by this method.<br><br>El hexaluminato de calcio (CaAl<sub>12</sub>O<sub>19</sub> o CA<sub>6</sub>) es el material más rico en Al<sub>2</sub>O<sub>3</sub> entre los compuestos intermedios en el sistema CaO-Al<sub>2</sub>O<sub>3</sub>. La formación de este aluminato se produce por la reacción entre el CaO y la Al<sub>2</sub>O<sub>3</sub> con la consecuente formación de compuestos intermedios con menores contenidos en Al<sub>2</sub>O<sub>3</sub> con el aumento de la temperatura (CaAl<sub>2</sub>O<sub>4</sub>, CaAl<sub>4</sub>O<sub>7</sub>,…). En este trabajo se ha estudiado la variación de los parámetros de sinterización para la obtención de hexaluminato de calcio (CA<sub>6</sub>) denso y puro por sinterización reactiva mediante Spark Plasma Sintering (Sinterización mediante corriente eléctrica pulsada o SPS), utilizando como reactivos Al<sub>2</sub>O<sub>3</sub> y CaCO<sub>3</sub> para su formación. Se han obtenido densidades cercanas a las teóricas y transformaciones superiores al 93% por este método.
Keywords