The performance on the method of welding in intermetallic alloy FeAl coating on the structural steel

Abstract

Implementation of new materials into industrial practice allows to build more durable and reliable machine parts suitable to operate at high temperature and other special conditions. The paper analyzes implementation of welding method to make intermetallic surface Fe40Al5CrTiB on material grade S235JR. The process was made with tungsten inert gas (TIG) and with the use of reserved polarity direct current (DC-). Welded sample was made as: single bead, multi bead and as multilayer. After the welding process, samples were tested with light microscopy (LM), scanning electron microscopy (SEM) and Vickers hardness (HV). This technology can by used to develop resistance surfaced in the power industry in the future. in polish Wykonanie metodą napawania powłoki ze stopu międzymetalicznego FeAl na stali konstrukcyjnej Wdrożenie nowych materiałów do praktyki przemysłowej pozwala na konstrukcję trwalszych i bardziej wytrzymałych części maszyn przeznaczonych do pracy w wysokiej temperaturze oraz ekstremalnych warunkach. W artykule analizowano zastosowanie metody napawania do wykonania napoiny ze stopu na osnowie fazy międzymetalicznej Fe40Al5CrTiB na powierzchni stali S235JR. Proces prowadzono metodą TIG w atmosferze gazu obojętnego przy zastosowaniu prądu stałego (DC-). Próbki napawano w trzech wariantach: jednościegowym, wielościegowym oraz wielowarstwowym. Po procesie napawania przeprowadzono badania za pomocą mikroskopu świetlnego (LM), elektronowego mikroskopu skaningowego oraz dokonano pomiarów twardości metodą Vickersa (HV). Technologia ta może być zastosowana w przyszłości, na przykład w przemyśle energetycznym do wytworzenia powierzchni żaroodpornych.

Keywords

• hardfacing
• TIG cladding
• intermetallic phase
• imperfection