Strong and ductile beta Ti–18Zr–13Mo alloy with multimodal twinning

Abstract

Body-centred cubic (BCC) Ti–18Zr–13Mo (wt%) alloy displays excellent yield strength (≈800 MPa), stable hardening (rate > 1500 MPa) and uniform ductility >18%, resulting from multi-TWIP (multiple twinning-induced plasticity) strengthening effect. This multimodal mechanisms include micro-scale {332} deformation twinning (DT), nano-scale {112} DT and a rare {5 8 11} DT mode. Martensitic phase transformation is completely suppressed and the sample stays a single-phase solid solution throughout the deformation. In situ electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) were used to characterize the multi-TWIP and dynamic Hall–Patch effect, with dislocation slip and large grain distortions at twin interfaces.

Keywords

• vacuum arc-melting beta ti
• deformation mechanisms
• twinning
• multimodal twip