Calcination Temperature Induced Structural, Optical and Magnetic Transformations in Titanium Ferrite Nanoparticles

Abstract

Titanium ferrite represents one of the most promising magnetic materials that exhibits optical absorption in both ultraviolet and visible spectral regions with a range of applications in photocatalysis, giant magnetoresistance, sensors, high-frequency modern power supplies, etc. Here in the present work, we report synthesizing titanium ferrite NPs via the co-precipitation method. As obtained ferrite nanopowders were characterized using XRD, UV-Visible absorption, Raman scattering, and variable sample magnetometer techniques. The crystalline size of NPs lies between 35 to 50 nm. The as-obtained nanopowder samples were calcined at 200, 500, 800 °C temperatures, and the resulting change in the optical, structural, and magnetic properties are investigated. The saturation magnetization of 500 °C calcined sample is higher than that calcined at 200 °C, but the magnetization value drastically becomes reduced for powder calcined at 800 °C temperature. The results of the present work can be used to understand the effects of annealing temperature on the structural and magnetic properties of other ferrite nanomaterials.

Keywords

• magnetic properties
• chemical co-precipitation
• Raman spectroscopy
• spinel ferrite