Laser Welding of UNS S33207 Hyper-Duplex Stainless Steel to 6061 Aluminum Alloy Using High Entropy Alloy as a Filler Material

Abstract

The high entropy alloy (HEA) filler used during the fabrication method determines the reliability of HEAs for steel-aluminum dissimilar alloy configuration. HEAs have a direct impact on the formation of intermetallic compounds (IMC) formed by the interaction of iron (Fe) and aluminum (Al), and influence the size of the joint’s interaction zone. A novel welding process for Fe-Al alloy joints was developed to prevent the development of a brittle iron-aluminum interface. This research involved investigation of the possibility of using HEA powdered filler. Fe5Co20Ni20Mn35Cu20 HEAs was used as a filler for the laser joining lap configuration joining hyper-duplex stainless steel UNS S33207 to aluminum alloy 6061. This HEA has unique properties, such as high strength, good ductility, and high resistance to corrosion and wear. A tiny portion of the stainless-steel area was melted by varying the welding parameters. The high-entropy alloy (HEA) with slow kinetic diffusion and large entropy was employed to aid in producing solid solution structures, impeding the blending of iron and aluminum particles and hindering the development of Fe-Al IMCs. The weld seam was created without the use of Fe-Al IMCs,. The specimen broke at the HEAs/Al alloy interface with a tensile-shear strength of 237 MPa. The tensile-shear strength achieved was 12.86% higher than for the base metal AA 6061 and 75.57% lower than for the UNS S33207 hyper-duplex stainless steel.

Keywords

• high entropy alloy
• hyper-duplex stainless steel
• laser welding
• aluminum alloy