Welding-induced corrosion and protective measures for clad rebars in neutral chloride environments

Abstract

Abstract Corrosion-resistant steel plays a vital role in marine steel structures. This study developed an SS304/HRB400 stainless-steel-clad rebar for application in a cross-sea bridge in Zhejiang Province. CO2 gas shielded welding was employed in the prefabricated steel structure, with SS304 steel as the welding wire. This study investigated the welding on the corrosion resistance of clad rebars and explored corrosion protection measures for welded joints.The results indicated that refined grains appeared in both stainless steel and carbon steel due to distinct dynamic recrystallization (DRX) during welding. The corrosion resistance, as determined by potentiodynamic polarization curve analysis of the material’s interaction with the solution ranked as follows: clad rebar (polished) > clad rebar welding (CRW) > painting the clad rebar after welding (PCRW) > clad rebar (unpolished) > carbon-steel welding (CSW) > carbon-steel bar > cold spraying zinc after clad rebar welding (ZCRW). However, an accelerated corrosion test with four samples for 600 s with a corrosion current of 0.8 A revealed minimal corrosion damage on zinc-coated surfaces. Hence, welding joints for clad steel structures are considered feasible and must be subject to cold zinc spraying after polishing to enhance their corrosion resistance.

Keywords

• Clad rebars welding (CRW)
• Electrochemical corrosion
• Dynamic recrystallization (DRX)
• Neutral chloride environment