Hydrogen absorption study of ti-based alloys performed by melt-spinning

Abstract

The hydrogen absorption and desorption of Ti53Zr27Ni20 icosahedral quasicrystal (ICQ) and Ti50Ni50 shape memory alloy (SMA) melt-spun ribbons was studied. Samples were exposed to hydrogen gas at 623 K and 4 MPa for 1000 minutes. The total capacity of hydrogen obtained for Ti53Zr27Ni20 and Ti50Ni50 was 3.2 and 2.4 wt. % respectively. The Thermal Desorption Spectrometry (TDS) of the hydrogenated alloys shows that both alloys start to desorb hydrogen around 750 K. X-ray diffraction (XRD) patterns, performed after hydrogenation, indicate a complete amorphization of the Ti53Zr27Ni20 i-phase alloy, while the Ti50Ni50 alloy remained crystalline after hydride formation.

Keywords

• hydrogen absorption
• Ti-Ni alloy
• Ti-Zr-Ni alloy