Materials & Design (Mar 2023)

Superior oxidation resistance of the chemically complex but structurally simple Ti-Al-Ta-Ce-Si-La-B-nitride

  • P.H. Mayrhofer,
  • S. Kagerer,
  • P. Polcik,
  • A. Kirnbauer

Journal volume & issue
Vol. 227
p. 111722

Abstract

Read online

Alloying (Ti,Al)N with Ta, CeSi2 or LaB6 is beneficial for both hardness and thermal stability. Here we show that their different mechanisms allow for a cumulative improvement when alloyed together, which is especially pronounced for the oxidation resistance. During isothermal oxidation treatments in ambient air at 900 °C (for up to 25 h), Ti0.44Al0.44Ta0.12N allows for a parabolic scale growth rate constant kp of 6.039 × 10-5 µm2/s. This is reduced to 2.074 × 10-5 and even 0.399 × 10-5 µm2/s when alloying with 2 mol% CeSi2 respectively CeSi2 + LaB6 (1 mol% each). The oxide scale growth kinetics for the latter can be even better described by a logarithmic or cubic law. In the as-deposited state the CeSi2 and CeSi2 + LaB6 alloyed (Ti,Al,Ta)N are single-phase fcc structured providing an indentation hardness of 32.6 ± 1.5 and 37.8 ± 1.5 GPa, combined with an indentation modulus of 496 ± 22 and 496 ± 14 GPa, respectively. After vacuum-annealing at 1000 °C, their hardness is still 33.0 ± 1.6 and 34.8 ± 1.1 GPa, and noticeable formation of hexagonal AlN and TaNx phases can only be detected by X-ray diffraction when annealed at temperatures above 1200 °C.Using CeSi2 and LaB6 instead of their elemental form is furthermore beneficial for the target production itself, as Ce and La are highly reactive.

Keywords