Characteristics of the Dynamic Recrystallization Behavior of Ti-45Al-8.5Nb-0.2W-0.2B-0.3Y Alloy during High Temperature Deformation

Abstract

The dynamic recrystallization (DRX) behavior of Ti-45Al-8.5Nb-0.2W-0.2B-0.3Y (at %) alloy has been investigated through hot compression tests. The tests were executed at a temperature range of 1000–1200 °C and a strain rate range of 0.001–1 s−1 under a true strain of 0.9. It was found that the α2 phase which is produced during heat treatment is reduced during hot compression due to thermo-mechanical coupling. The value of the activation energy is 506.38 KJ/mol. With the increase in deformation temperature and the decrease in strain rate, DRX is more likely to occur, as a result of sufficient time and energy for the DRX process. Furthermore, the volume fraction of high angle grain boundaries increases to 89.01% at a temperature of 1200 °C and the strain rate of 0.001 s−1, meaning completely dynamic recrystallization. In addition, DRX is related to the formation of twin boundaries. The volume fraction of twin boundaries rises to 16.93% at the same condition of completely dynamic recrystallization.

Keywords

• titanium aluminides
• hot compression
• dynamic recrystallization
• microstructure