Eco‐Friendly and High Performance Supercapacitors for Elevated Temperature Applications Using Recycled Tea Leaves

Abstract

Abstract Used tea leaves are utilized for preparation of carbon with high surface area and electrochemical properties. Surface area and pore size of tea leaves derived carbon are controlled by varying the amount of KOH as activating agent. The maximum surface area of 2532 m2 g−1 is observed, which is much higher than unactivated tea leaves (3.6 m2 g−1). It is observed that the size of the electrolyte ions has a profound effect on the energy storage capacity. The maximum specific capacitance of 292 F g−1 is observed in 3 m KOH electrolyte with outstanding cyclic stability, while the lowest specific capacitance of 246 F g−1 is obtained in 3 m LiOH electrolyte at 2 mV s−1. The tea leaves derived electrode shows almost 100% capacitance retention up to 5000 cycles of study. The symmetrical supercapacitor device shows a maximum specific capacitance of 0.64 F cm−2 at 1 mA cm−2 and about 95% of specific capacitance is retained after increasing current density to 12 mA cm−2, confirming the high rate stability of the device. An improvement over 35% in the charge storage capacity is seen when increasing device temperature from 10 to 80 °C. The study suggests that used tea leaves can be used for the fabrication of environment friendly high performance supercapacitor devices at a low cost.

Keywords

• activated carbon
• biowaste
• energy storage
• supercapacitor
• tea leaves