Open Chemistry (Apr 2021)

Sodium borohydride (NaBH4) as a high-capacity material for next-generation sodium-ion capacitors

  • Jeżowski Pawel,
  • Crosnier Olivier,
  • Brousse Thierry

DOI
https://doi.org/10.1515/chem-2021-0040
Journal volume & issue
Vol. 19, no. 1
pp. 432 – 441

Abstract

Read online

Energy storage is an integral part of the modern world. One of the newest and most interesting concepts is the internal hybridization achieved in metal-ion capacitors. In this study, for the first time we used sodium borohydride (NaBH4) as a sacrificial material for the preparation of next-generation sodium-ion capacitors (NICs). NaBH4 is a material with large irreversible capacity of ca. 700 mA h g−1 at very low extraction potential close to 2.4 vs Na+/Na0. An assembled NIC cell with the composite-positive electrode (activated carbon/NaBH4) and hard carbon as the negative one operates in the voltage range from 2.2 to 3.8 V for 5,000 cycles and retains 92% of its initial capacitance. The presented NIC has good efficiency >98% and energy density of ca. 18 W h kg−1 at power 2 kW kg−1 which is more than the energy (7 W h kg−1 at 2 kW kg−1) of an electrical double-layer capacitor (EDLC) operating at voltage 2.7 V with the equivalent components as in NIC. Tin phosphide (Sn4P3) as a negative electrode allowed the reaching of higher values of the specific energy density 33 W h kg−1 (ca. four times higher than EDLC) at the power density of 2 kW kg−1, with only 1% of capacity loss upon 5,000 cycles and efficiency >99%.

Keywords