Tribological performance of novel nickel-based composite coatings with lubricant particles

Abstract

Abstract The present study is focused on the evaluation of the tribological performance of novel Ni/hBN and Ni/WS2 composite coatings electrodeposited from an additive-free Watts bath with the assistance of ultrasound. Lubricated and non-lubricated scratch tests were performed on both novel composite coatings and on standard Ni deposits used as a benchmark coating to have an initial idea of the effect of the presence of particles within the Ni matrix. Under lubricated conditions, the performance of the Ni/hBN composite coating was very similar to the benchmark Ni coating, whereas the Ni/WS2 behaved quite differently, as the latter did not only show a lower coefficient of friction, but also prevented the occurrence of stick-slip motion that was clearly observed in the other coatings. Under non-lubricated conditions, whereas the tribological performance of the Ni/hBN composite coating was again very similar to that of the benchmark Ni coating, the Ni/WS2 composite coatings again showed a remarkable enhancement, as the incorporation of the WS2 particles into the Ni coating not only resulted in a lower coefficient of friction, but also in the prevention of coating failure.

Keywords

• nickel
• tungsten disulphide
• hexagonal boron nitride
• composite coatings
• solid lubricant
• tribology