Efficient CO2 adsorption using chitosan, graphene oxide, and zinc oxide composite

Abstract

Abstract This study was deeply focused on developing a novel CTS/GO/ZnO composite as an efficient adsorbent for CO2 adsorption process. To do so, design of experiment (DOE) was done based on RSM-BBD technique and according to the DOE runs, various CTS/GO/ZnO samples were synthesized with different GO loading (in the range of 0 wt% to 20 wt%) and different ZnO nanoparticle’s loading (in the range of 0 wt% to 20 wt%). A volumetric adsorption setup was used to investigate the effect of temperature (in the range of 25–65 °C) and pressure (in the range of 1–9 bar) on the obtained samples CO2 uptake capability. A quadratic model was developed based on the RSM-BBD method to predict the CO2 adsorption capacity of the composite sample within design space. In addition, CO2 adsorption process optimization was conducted and the optimum values of the GO, ZnO, temperature, and pressure were obtained around 23.8 wt%, 18.2 wt%, 30.1 °C, and 8.6 bar, respectively, with the highest CO2 uptake capacity of 470.43 mg/g. Moreover, isotherm and kinetic modeling of the CO2 uptake process were conducted and the Freundlich model (R2 = 0.99) and fractional order model (R2 = 0.99) were obtained as the most appropriate isotherm and kinetic models, respectively. Also, thermodynamic analysis of the adsorption was done and the ∆H°, ∆S°, and ∆G° values were obtained around − 19.121 kJ/mol, − 0.032 kJ/mol K, and − 9.608 kJ/mol, respectively, indicating exothermic, spontaneously, and physically adsorption of the CO2 molecules on the CTS/GO/ZnO composite’s surface. Finally, a renewability study was conducted and a minor loss in the CO2 adsorption efficiency of about 4.35% was obtained after ten cycles, demonstrating the resulting adsorbent has good performance and robustness for industrial CO2 capture purposes.