Effects of Al3Ni compound on localized plastic deformation and creep strain of Al/Si hypoeutectic material

Abstract

Abstract The mechanical resistance of AS10/xNi hypoeutectic alloy with (x = 0.05% and 0.1%) has been investigated. Vickers hardness (HV) was determined for the samples before and after sintering. All samples were subjected to a compressive creep test at a constant temperature of 298 K and a constant load of 45 MPa. Creep parameters, such as creep rate, sensitivity (m), time exponent (n), β, and ɣ have been calculated and related to the Ni content. Microstructure investigation was conducted using the scanning electron microscope technique (SEMT). After sintering, the results showed that there was a significant improvement in the hardness with the addition of nickel. There is an increase in creep resistance as a result of the distribution of Al3Ni chemical compound across grain boundaries, which stops additional dislocation movement and hence reduces the creep rate.