The Effect of Nb-Content on the Microstructures and Corrosion Properties of CrFeCoNiNb_x High-Entropy Alloys

Abstract

This work studied the effect of niobium-content on the microstructures, hardness, and corrosion properties of CrFeCoNiNbx alloys. Results indicated that the microstructures of these alloys changed from granular structures (CrFeCoNi alloy) to the hypereutectic structures (CrFeCoNiNb0.2 and CrFeCoNi0.4 alloys), and then to the hypoeutectic microstructures (CrFeCoNiNb0.6 and CrFeCoNi alloys). The lattice constants of the major two phases in these alloys, fcc and Laves phases (hcp), increased with the increasing of Nb-content because of solid-solution strengthening. The hardness of CrFeCoNiNbx alloys also had the same tendency. Adding niobium would slightly lessen the corrosion resistance of CrFeCoNiNbx alloys in 1 M deaerated sulfuric acid and 1 M deaerated sodium chloride solutions, but the CrFeCoNiNbx alloys still had better corrosion resistance in comparison with commercial 304 stainless steel. In these dual-phased CrFeCoNiNbx alloys, the fcc phase was more severely corroded than the Laves phase after polarization tests in these two solutions.

Keywords

• crfeconinb_x alloys
• microstructure
• hardness
• corrosion property