Constructing a Sr²⁺-Substituted Surface Hydroxyapatite Hexagon-Like Microarray on 3D-Plotted Hydroxyapatite Scaffold to Regulate Osteogenic Differentiation

Abstract

Surface topography and chemical characteristics can regulate stem cell proliferation and differentiation, and decrease the bone-healing time. However, the synergetic function of the surface structure and chemical cues in bone-regeneration repair was rarely studied. Herein, a strontium ion (Sr2+)-substituted surface hydroxyapatite (HA) hexagon-like microarray was successfully constructed on 3D-plotted HA porous scaffold through hydrothermal reaction to generate topography and chemical dual cues. The crystal phase of the Sr2+-substituted surface microarray was HA, while the lattice constant of the Sr2+-substituted microarray increased with increasing Sr2+-substituted amount. Sr2+-substituted microarray could achieve the sustainable release of Sr2+, which could effectively promote osteogenic differentiation of human adipose-derived stem cells (ADSCs) even without osteogenic-induced media. Osteogenic characteristics were optimally enhanced using the higher Sr2+-substituted surface microarray (8Sr-HA). Sr2+-substituted microarray on the scaffold surface could future improve the osteogenic performance of HA porous scaffold. These results indicated that the Sr2+-substituted HA surface hexagon-like microarray on 3D-plotted HA scaffolds had promising biological performance for bone-regeneration repair scaffold.

Keywords

• 3D plotting
• hydroxyapatite scaffold
• hexagon-like microarray
• Sr²⁺-substituted
• osteogenic differentiation