Materials (Jan 2023)
Investigating Ultrasonic Pulse Velocity Method for Evaluating High-Temperature Properties of Non-Sintered Hwangto-Mixed Concrete as a Cement Replacement Material
Abstract
Research on alternative cement materials is active worldwide, and in terms of fire safety, research on the evaluation of high-temperature properties of alternative materials is very important. Studies on concrete mixed with hwangto have been conducted by several researchers, but studies on high-temperature properties are lacking. Therefore, in this study, we evaluated the mechanical properties of concrete by partially replacing cement with non-sintered hwangto (NSH) at high temperatures. Normal concrete without NSH mixing and non-sintered hwangto concrete (NSHC) with HNT replacement were prepared as the specimens. The W/B of the concrete was set to 41 and 33, whereas the NSH replacement ratio was 15 and 30% of the cement. The target heating temperatures were set to 20, 100, 200, 300, 500, and 700 °C, and the heating rate was maintained at 1 °C/min. The following were calculated to evaluate the mechanical properties of the specimens: mass loss, compressive strength, ultrasonic pulse velocity (UPV), and modulus of elasticity. After analyzing the correlation between residual compressive strength and UPV, we proposed a compressive strength prediction model using different values of W/B for NSHC. Experimental results suggest that mass loss (%) shows a decreasing trend as NSH increases. In terms of residual compressive strength, residual compressive strength at W/B 41 increased with NSH replacement, whereas residual compressive strength values for W/B 33 were observed regardless of NSH replacement. Residual UPV showed a similar trend, regardless of the NSH replacement ratio, and residual modulus of elasticity was low at all W/B ratios as NSH replacement increased. A linear equation with a high correlation coefficient (R2) was proposed to predict compressive strength, and the linear value of W/B 41 was slightly higher than that of W/B 33.
Keywords