Effect of process parameters on biopolymer films based on sunflower oil cake

Abstract

The purpose of this paper is the synthesis and characterization of biodegradable composite films based on whole sunflower oil cake, as well as the effect of process parameters (pH and temperature)on the film properties obtained. Films were synthesized at different temperatures (room temperature, 60 °C and 90 °C) and pH values (10 and 12). The film samples obtained were characterized by the mechanical, barrier and physicochemical properties determination. The experimental results showed that the tensile strength values increased with temperature and pH value increments, whereas the sample with the highest elongation at break value was 60 °C/pH12. The water vapour permeability values were uniform (8.62 g/m2h - 11.63 g/m2h), and lower values were recorded in samples synthesized at higher temperatures. The results obtained relative to light transmission were uniform, and the maximum transmission value was reached at 800 nm (24.1- 35.7 %). The values obtained for swelling and solubility parameters are characteristic of the nature of biopolymer films.

Keywords

• biopolymers
• sunflower oil cake
• process parameters
• characterization