Oxidation Mechanism of Al-Sn Bearing Alloys

Abstract

Oxidation of Al-Sn bearing alloy occurs during production, processing and use, which reduces both alloy performance and performance of coatings applied to the alloy surface. Therefore, the oxidation mechanism of Al-Sn bearing alloy is studied at 25, 180, 300, and 500 °C. The oxidation morphologies of the alloy were observed by scanning electron microscopy (SEM), and the oxidation products were determined by X-ray diffraction (XRD). The oxidation weight gain curves were obtained by thermogravimetric analysis. The experimental results show that: Al-Sn bearing alloy is oxidized quickly to form Al2O3. As the oxidation temperature increases, Sn phase start to precipitate along the grain boundary and form networked spheroids of Sn on the alloy surface. The amount of precipitation increases with further increase of the oxidation temperature. Cracks and holes are left in the alloy. The oxide layer is mainly composed of Sn, SnO2, and Al2O3. At 25 °C, oxidation rate of Al-Sn alloy approach zero. At 180, 300, and 500 °C, the oxidation rate increases quickly conforming to a power function, and eventually remains stable at about 3 × 10−6 mg·mm−2·s−1.

Keywords

• Al-Sn bearing alloy
• oxidation mechanism
• oxidation kinetics
• precipitation