Some physical and mechanical properties of particle boards produced with hazelnut husk and astragalus (Astragalus membranaceus) plant

Abstract

In this study, under laboratory conditions, hazelnut husk and astragalus plant were mixed separately into black pine wood chips, and multi-purpose boards were produced from the obtained chips with urea formaldehyde glue. After the hazelnut husk and astragalus plant were dried and ground, they were added to the chip and glue mixture in certain proportions. Hazelnut husk mixture ratios were applied as 100 %; 0 %, 75 %; 25 %, 50 %; 50 %, 25 %; 75 %, 0 %; 100 % to black pine wood chip in the particle board mixture. These ratios were made in the same way for the astragalus plant. From these mixtures, chipboard blanks of 16 mm thickness and densities between 0,68 g/cm3 and 0,72 g/cm3 were produced. Density, moisture content, thickness increase, water intake, bending strength, modulus of elasticity in bending and tensile strength perpendicular to the surface were tested in physical and mechanical experiments. According to the results obtained, as the participation rate of hazelnut shells and astragalus increased, the durability properties of the panels decreased. At the same time, it shows that the technological properties of the panels produced by adding up to 25 % astragalus plant and hazelnut shells to the mixture comply with the standards.

Keywords

• Astragalus plant
• black pine wood chip
• hazelnut husk
• mechanical properties
• particle board
• physical properties.