Role of Stabilization Heat Treatment Inducing γ′-γ″ Co-Precipitates and η Phase on Tensile Behaviors of Inconel 706
Abstract
Inconel 706 (IN706) alloy is commonly used in aircraft engines and power plant components that must meet very high performance requirements. The stabilization treatment has a significant effect on the precipitation and evolution of the reinforcing phases of the alloy, favoring the creep properties and adversely affecting the room-temperature tensile properties. However, the mechanism of the effect of the stabilization treatment on the mechanical properties of the alloys remains unclear. In this study, the effect of stabilization treatment time on the microstructure and tensile properties of IN706 alloy was investigated. The results showed that as the stabilization time gradually increased, the tensile strength remained basically unchanged (about 1250 MPa), the yield strength decreased from 1031 MPa to 985 MPa, and the plasticity decreased from 28.2% to 20.2%. The stabilization treatment induces the precipitation of granular, rod-shaped, and needle-like η phases at grain boundaries, accompanied by the appearance of a precipitate free zone (PFZ). Since the η phase is enriched with Ti and Nb, its precipitation along the grain boundary results in the depletion of Ti and Nb in the surrounding regions, thereby constraining the precipitation of the γ′ and γ″ phases, resulting in the appearance of PFZ. With increasing stabilization time, the size increase and volume fraction decrease in γ′-γ″ co-precipitates due to the precipitation of η-phase precipitates, leading to a decrease in their yield strength. Combined with in situ tensile tests, it was found that the decrease in the elongation of the stabilization treatment samples was due to the presence of η phase at the grain boundaries, which induced stress concentration and cracking at the grain boundaries. The results show that the mechanical properties of the material were gradually enhanced as the stabilization time decreased. This means it can help to choose the suitable process for IN706 alloy in different service conditions.
Keywords