Attempts to Obtain Material Based on Polyvinyl Alcohol with Barrier Properties against Water Vapor

  • Lucica Maria Pop,
  • Anca Mihaly Cozmuta,
  • Camelia Nicula,
  • Leonard Mihaly Cozmuta,
  • Anca Peter

DOI
https://doi.org/10.3390/app14104310
Journal volume & issue
Vol. 14, no. 10
p. 4310

Abstract

Read online

The purpose of this study was to obtain a biodegradable film based on polyvinyl alcohol with reduced water vapor permeability. The hydrophobic character of the films was achieved by incorporating beeswax, vegetable bio-surfactant, citric acid as a cross-linking agent, and glycerol to provide elasticity, along with the application of thermal treatment. Water vapor permeability was determined gravimetrically. The results indicated that all films produced had lower water vapor permeability compared to unmodified or untreated polyvinyl alcohol films. The barrier to water vapor varied directly with the mass of beeswax used, and the homogeneous dispersion of beeswax in the polyvinyl alcohol matrix was essential for achieving an efficient hydrophobic film. The best performing-material exhibited a water vapor permeability 5.15 times lower than that of the neat polyvinyl alcohol and 15 times higher than that of polyethylene. Considering the fact that the water vapor barrier property of neat polyvinyl alcohol was 78 times lower than that of polyethylene, the combination of beeswax, citric acid, and vegetable bio-surfactant—along with thermal treatment—can be a viable solution to reduce the hygroscopicity of polyvinyl alcohol-based films.

Keywords