Effect of Tempering Time on Carbide Evolution and Mechanical Properties of a Nb-V-Ti Micro-Alloyed Steel

Abstract

The evolution of the microstructure, the precipitation behavior, and the mechanical performances of Nb-V-Ti micro-alloyed steel prepared under different tempering time were studied using transmission electron microscopy (TEM), X-ray diffraction (XRD), and mechanical tests. It was found that the width of the martensite laths increases with the increasing tempering time. Several kinds of carbides, including M3C, M2C, M23C6, M7C3, and MC particles, were identified after tempering. The MC carbides remain stable during tempering, but the transformation behavior of other carbides was identified. The transformation sequence can be summarized as: M3C → M2C → M7C3 → M23C6. The strength decreases and the Charpy impact toughness increases gradually with the increase in the tempering time. The ultimate strength (UTS) decreases from 1231 to 896 MPa, and the yield strength (YS) decreases from 1138 to 835 MPa. The −40 °C Charpy impact toughness increases from 20 to 61 J as the tempering time increases from 10 min to 100 h. The evolution of carbides plays an important role in their mechanical performances.

Keywords

• carbide
• tempering time
• Nb-V-Ti micro-alloyed steel
• mechanical performance