Study on Structure and Anti-UV Properties of Sericin Cocoons

Abstract

Through biogenetic engineering, the posterior silk glands of Bombyx mori larvae are degenerated, and only the middle silk glands are retained to secrete sericin to produce sericin fibers, so as to obtain sericin cocoons with high sericin content (>98.5%). For this paper, sericin cocoons were studied, and the morphological structure characteristics and properties of sericin cocoons and common Bombyx mori cocoons were compared and analyzed through such modern test techniques as SEM, FTIR, and XRD. Results show that sericin cocoons have the basic morphological structure of cocoons, but because of the brittleness and hardness of sericin, the ssericin cocoons have poor integrity with a thermal decomposition rate that is higher than that of cocoons; the two cocoons are of a similar protein structure, with both α-helix and β-sheet structures, and dominantly the β-sheet structure; and the crystallinity of sericin cocoons (10.48%) is lower than that of the common Bombyx mori cocoons (27.10%). Sericin was extracted from both cocoons to obtain a mixed sericin solution respectively, which were coated on base fabrics of polyester taffeta (210T) for coating finish and subjected to qualitative research for their anti-UV properties. The base fabrics coated with mixed sericin solutions of sericin cocoons and Bombyx mori cocoons have an anti-UV performance index (UPF) of 23.9% and 22.5% respectively, which are higher than that of the base fabric (8.9%)..

Keywords

• sericin cocoon
• sericin fiber
• morphological structure
• thermal property
• anti-uv